Conductive Composite Fibres from Reduced Graphene Oxide and Polypyrrole Nanoparticles

Journal of Materials Chemistry B 2016 Volume 4, Issue 6, Pages 1142-1179

Continuous composite fibres composed of polypyrrole (PPy) nanoparticles and reduced graphene oxide (rGO) at different mass ratios were fabricated using a single step wet-spinning approach. The electrical conductivity of the composite fibres increased significantly with the addition of rGO. The mechanical properties of the composite fibres also improved by the addition of rGO sheets compared to fibres containing only PPy. The ultimate tensile strength of the fibres increased with the proportion of rGO mass present. The elongation at break was greatest for the composite fibre containing equal mass ratios of PPy nanoparticles and rGO sheets. L929 fibroblasts seeded onto fibres…

From nanoparticles to fibres: effect of dispersion composition on fibre properties

Journal of Nanoparticle Research 2015 Volume 17, Issue 237, Pages 237ff

A polyvinyl alcohol (PVA)-stabilized polypyrrole nanodispersion has been optimised for conductivity and processability by decreasing the quantity of PVA before and after synthesis. A reduction of PVA before synthesis leads to the formation of particles with a slight increase in dry particle diameter (51 ± 6 to 63 ± 3 nm), and conversely a reduced hydrodynamic diameter. Conductivity of the dried nanoparticle films was not measureable after a reduction of PVA prior to synthesis. Using filtration of particles after synthesis, PVA content was sufficiently reduced to achieve dried thin film conductivity of 2 S cm−1, while the electroactivity of the…